“Pengaruh Proses Pengelasan Tungsten Inert Gas (Tig) Terhadap Kekuatan Tarik, Struktur Mikro Dan Uji Impact Pada Baja Din 1.2316”.

Reza Arifianto, . (2018) “Pengaruh Proses Pengelasan Tungsten Inert Gas (Tig) Terhadap Kekuatan Tarik, Struktur Mikro Dan Uji Impact Pada Baja Din 1.2316”. Universitas Pamulang, Tangerang Selatan.

[img] Text
COVER.docx
Restricted to Registered users only

Download (330kB)
[img] Text
BAB I.docx
Restricted to Registered users only

Download (37kB)
[img] Text
BAB II.docx
Restricted to Registered users only

Download (7MB)
[img] Text
BAB III.docx
Restricted to Registered users only

Download (8MB)
[img] Text
BAB IV.docx
Restricted to Registered users only

Download (3MB)
[img] Text
BAB V.docx
Restricted to Registered users only

Download (28kB)
[img] Text
JURNAL.docx
Restricted to Registered users only

Download (16MB)

Abstract

Telah berhasil dilakukan proses pengelasan pada ampere 70A, 80A, 90A pada baja DIN 1.2316 dengan pengujian uji tarik, uji impact dan struktur mikro. Dari proses tersebut, dianalisa kandungan unsur pada baja tersebut menggunakan SEM-EDX. Analisa morfologi dengan mikroskop optik, analisa struktur mikro dengan XRD dan tingkat kekuatan uji (HV) . Hasil analisa komposisi dari sampel standar menunjukan bahwa unsur Fe dan Cr merupakan yang dominan, sedangkan Mo, Ni, Si, dan Mn sebagai minoritas. Pada uji tarik di peroleh 40% sebelum putus dan 70A, 80A, 90A mencapai 22,5%, 25%, 35%. Kata kunci : Baja DIN 1.2316, kekuatan Uji tarik, Uji impact dan struktur mikro.

Item Type: Other
Subjects: H Social Sciences > HB Economic Theory
L Education > L Education (General)
Depositing User: Bisma Lubis
Date Deposited: 26 Apr 2018 04:53
Last Modified: 26 Apr 2018 04:53
URI: http://eprints.unpam.ac.id/id/eprint/3698

Actions (login required)

View Item View Item